Structural and Optical Properties of ZnO/PMMA Nanocomposite
A. Aadila1, 2, a, N. A. M. Asib1, 2, b, A. N. Afaah1, 2, c, R. Mohamed4, d,
M. Rusop1, 3, e and Z. Khusaimi1, 2, f
1Nano-SciTech Centre, Institute of Science, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor, Malaysia
2Faculty of Applied Sciences, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor, Malaysia
3NANO-Electronic Centre, Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor, Malaysia
4Faculty of Applied Sciences, Universiti Teknologi MARA Cawangan Pahang, Lintasan Semarak, 26400 Bandar Pusat Jengka, Pahang, Malaysia
[email protected], [email protected], [email protected], [email protected], [email protected], [email protected]
Keywords: ZnO, solution-immersion method, PMMA, spin coating, nanocomposite
Abstract. UV filter is an interesting and challenging application in industries. Hence, ZnO-PMMA
nanocomposite thin films have been chosen to achieve above mentioned characteristics [1]. In this
study, fabrication of ZnO on PMMA glass substrate successfully prepared by using the solution-
immersion method. Layer by layer of poly (methyl methacrylate) (PMMA) was deposited on a glass
substrate using the spin coating technique by dissolving PMMA in toluene. Various layers of
PMMA were varied to 1, 3, 5 and 7 layers. The structural and optical properties of ZnO/PMMA
nanocomposite were then characterized by Field Emission Scanning Electron Microscope (FESEM)
and Photoluminescene (PL) Spectroscopy. From FESEM result, shape of nanorod unclearly seen as
the layer deposited of PMMA increase and from EDAX show oxygen element have highest atomic
percentage 65.50 %. 7 layer of deposited PMMA show highest intensity compare to other layers in
green region at 577.32 nm for PL measurement.
Introduction
Zinc oxide (ZnO) is very promising semiconductor due to unique properties in near-UV region,
electric conductivity and optical transparency [2]. Among one dimensional (1-D) nanomaterials,
ZnO has received extensive attention due to its large direct band gap semiconductor properties (3.3 ̴
3.4 eV) [3, 4] and large exciton binding energy (60 meV) [4, 5]. ZnO has an optical band gap in the
UV region and makes it an extremely efficient UV absorber. ZnO can be synthesized in various
synthetic paths such hydrothermal and solvothermal methods, mircoemulsion, sol-gel method, and
thermal decomposition of precursors [6].
Polymer is flexible lightweight materials and can be produced into thin films at a low cost. They
can be easily processed and shaped into thin films using different methods such dip-coating, spin-
coating, film-casting and printing [7]. Poly (methyl methacrylate) (PMMA) is a type of polymer
which is an optically clear amorphous thermoplastic [2, 6, 8]. It is frequently preferred because of
its moderate properties, easy handling and processing, and low cost [9]. However, PMMA does not
filter ultraviolet (UV) light. So, to overcome the deficiency, semiconductor nanocrystals with large
band gap such as TiO2, ZnO and ZnS can be introduced to PMMA matrix, which can be applied in
transparent UV-protective coatings or UV-shielding windows [10]. Furthermore, the nano
ZnO/PMMA composites have potential applications in UV protecting sheets and films, transparent
barrier or protective layers, antireflection coatings and as materials with increase thermal stability
[11]. The present study, optical properties of ZnO/PMMA nanocomposite was investigated.
Advanced Materials Research Vol. 832 (2014) pp 602-606Online available since 2013/Nov/21 at www.scientific.net© (2014) Trans Tech Publications, Switzerlanddoi:10.4028/www.scientific.net/AMR.832.602
All rights reserved. No part of contents of this paper may be reproduced or transmitted in any form or by any means without the written permission of TTP,www.ttp.net. (ID: 129.110.33.9, Univ of Texas at Dallas, Richardson, United States of America-27/05/14,14:17:28)
Experimental Method
Zinc nitrate hexahydrate Zn (NO3).6H2O mixed with hexamethylenetetramine (HMTA) (CH4N2O)
where HMTA as a stabilizer. While, PMMA solution were prepared by dissolve in toluene. Both of
the solutions were stirred for 24 hours at 60 °C for 1 hour. 6 nm of platinum was sputter coated for
24 s on glass substrate. Layer by layer of PMMA was deposited on glass substrate using spin
coating technique. Substrate deposited with PMMA was immersed in zinc solution by immersion
method for 4 hours. After immersion, the substrate was annealed for 20 minutes at 120 °C.
Fig. 1, Configuration of deposited PMMA layer on glass substrate
Subsequently, the samples were cooled at room temperature. Then, samples were characterized by
using Field Emission Scanning Electron Microscope (FESEM) and Photoluminescene (PL)
Spectroscopy.
Result and Discussion
Field Emission Scanning Electron Microscope (FESEM). The surface morphologies of
ZnO/PMMA nanocomposite on different layer of deposited PMMA substrate were characterized by
FESEM (JEOL JSM-7600F). The samples were taken at accelerating voltage of 5.0 kV. All the
samples were coated with platinum to minimize the charging effect. For Fig. 2(a) 1 layer and 2(b) 3
layers, nanorod of ZnO can be clearly seen compared to (c) 5 layers and (d) 7 layers. As layer of
deposited PMMA increase, shapes of ZnO nanorod started to deform. So, layer of PMMA on
substrate effect the shape of nanorod. The presence of ZnO and PMMA particles was be proven by
using EDAX analysis.
(a) 1 layer PMMA
(b) 3 layers PMMA
Advanced Materials Research Vol. 832 603
(c) 5 layers PMMA
(d) 7 layers PMMA
Fig. 2, FESEM image of ZnO/PMMA nanocomposite on different layer of deposited PMMA; (a) 1
layer PMMA, (b) 3 layer PMMA, (d) 5 layers PMMA and (d) 7 layers PMMA
Fig. 3, Energy Dispersive Analysis X-Ray (EDAX) spectrum of ZnO/PMMA nanocomposite
The Energy Disperse Analysis X-Ray (EDAX) was used to analyze the compositional of
nanocomposite material. Fig. 3 show EDAX spectrum of ZnO/PMMA nanocomposite for 1 layer of
deposited PMMA polymer. From Fig. 3, highest peak showed oxygen element with 65.50 % atomic
weight percentage due to oxygen presence in both ZnO compound and PMMA polymer. While
carbon element represent the structure of PMMA [12] with weight percentage 26.26 %. Pt element
contributed to the sample coating with platinum. While, for Si (4.61 %) and Mg (0.47 %) elements
might be due to the contamination of samples which originated from the furnace during annealing
process. The atomic percentage of significant elements in ZnO/PMMA nanocomposite is
summarized in Table 1.
604 Nanoscience, Nanotechnology and Nanoengineering
Table 1, Energy Disperse Analysis X-Ray (EDAX)
Element Atomic Percentage (%)
Oxygen (O) 65.50
Carbon (C) 26.26
Zinc (Zn) 3.05
Platinum (Pt) 0.12
Photoluminescene (PL) Spectroscopy. Photoluminescence (PL) is a sensitive technique for
examining the sample quality, especially its optical properties [7]. PL spectrum shows a wide and
intense emission band covering the whole 400 - 700 nm visible area with three highest peaks. The
broad PL emission band located in the visible region may be related to induced emission from some
defects such as oxygen vacancies and zinc interstitials [10].
Fig. 4, Intensity versus wavelength of ZnO/PMMA nanocomposite
Fig. 4 shows intensity of ZnO/PMMA nanocomposite with different layer of deposited PMMA on
glass substrate. 7 layer of PMMA show highest intensity compared to other layers which
wavelength at 416.05 nm is due to excitonic transition. The green emission at 577.32 nm (2.16 eV)
has an energy smaller than the band gap of ZnO (3.2eV) which this peak is related to oxygen defect
[13], a result of the recombination of a photogenerated hole with an electron occupying the oxygen
vacancy defect states [4]. While, at 635.71 nm is due to surface electrons and other imperfections
[14]. Therefore, as the deposited layer of PMMA on substrate decrease, the intensity of
ZnO/PMMA nanocomposite increases in visible region.
Conclusion
ZnO/PMMA nanocomposite was successfully prepared by using sol-gel spin coating method. From
FESEM, shape of ZnO nanorod deform as the layer of deposited PMMA increase and EDAX
analysis showed oxygen element have highest atomic percentage due to oxygen presence in both of
ZnO compound and PMMA polymer. From PL measurement, the intense peak was at 577.32 nm in
green region for 7 layer of PMMA which can be concluded that PL intensity increase as the layer of
deposited PMMA polymer decrease.
Advanced Materials Research Vol. 832 605
Acknowledgement
Grateful to Universiti Teknologi MARA for the support and also thanks to Fundamental Research
Grant Scheme 600-RMI/FRGS 5/3 (18/2012) for financial support. Thanks to NANO-Scitech
Centre and NANO-Electronic Centre colleagues for their helpful support and encouragement.
References
[1] A. K. Govindaraj, J. B. B. Rayappan, B. G. Jeyaprakash, Preparation and Characterization of
Metal Oxide : PMMA Composite Thin Films, J. of App. Sci. 16 (2012) 1766-1768.
[2] A. Anzlovar, Z. C. Orel, M. Zigon, Sub Micrometer and Nano ZnO as Filler in PMMA
Materials. Ori. Sci. Article. 3 (2011) 269-274.
[3] S. L. Patil, S. G. Pawar, A. T. Mane, M. A. Chougule, V. B. Patil, Nanocrystalline ZnO thin
films: optoelectronic and gas sensing properties. J Mater Sci: Mater Electron. 21 (2010) 1332–1336.
[4] A. Azlinda, Z. Khusaimi, S. Abdullah, M. Rusop, Characterization of Urea versus HMTA in
the Preparation of Zinc Oxide Nanostructures by Solution-Immersion Method Grown on Gold-
Seeded Silicon Substrate, Advanced Material Research. 364 (2012) 45-49.
[5] M. H. Mamat, M. Z. Musa, N.D.M. Sin, M.Rusop, Characteristics of Aligned Aluminum-
Doped Zinc Oxide Nanorod Arrays via a Novel Sonicated Sol-Gel Immersion, IEEE Symposium on
Industrial Electronics and Applications. 25-28 (2011) 463-467.
[6] A. Anzlovar, K. Kogej, Z. Crnjak Orel, M. Zigon, Polyol mediated nano size zinc oxide and
nanocomposites with poly(methyl methacrylate), Express Polymer Letters. 5 (2011) 604–619.
[7] S. Sharma, R. Vyas, S. Shrivastava, Y. K. Vijay, Effect of Swift Heavy Ion Irradiation on
Photoluminescence Properties of ZnO/PMMA Nanocomposite Films, Physica B. 406 (2011) 3230-
3233.
[8] S. Wacharawichanant, N. Thongbunyoung, P. Churdchoo, T. Sookjai, Effect of Zinc Oxide
on the Morphology and Mechanical Properties of Poly(Styrene-co-Acrylonitrile)/Poly(Methyl
Methacrylate)/Zinc Oxide Composites, Sci. J. UBU. 1 (2010) 21-26.
[9] R. Rajan Prakash, S. Pandiarajan, Dr. P. Venkatesh, Member IEEE, Dr. N. Kamaraj,
Performance Analysis of PMMA - TiO2 Nanocomposite Dielectrics, Proceedings of ICETECT.
7926 (2011) 46-49.
[10] L. Zhang, F. Li, Y. Chen, X. Wang, Synthesis of transparent ZnO/PMMA nano composite
films through free-radical copolymerization of asymmetric zinc methacrylate acetate and in-situ
thermal decomposition, Journal of Luminescence. 131 (2011) 1701-1706.
[11] M. M. Demir, K. Koynov, U. Akbey, C. Bubeck, I. Park, I. Lieberwirth, G.Wegner,
Nanocomposites as an Effective UV Absorber with Nano Size Zinc Oxide and PMMA,
Macromolecules. 40 (2007) 1089-1100.
[12] M. Dixit, S. Gupta, V. M. Thur, K. Rathore, K. Sharma, N. S. Saxena, Study of Glass
Transition Temperature of PMMA and CdS-PMMA Composite, Chalcogenide Letters. 6 (2009)
131-136.
[13] Z. Khusaimi, S. Amizam, H. A. Rafaie, M. H. Mamat, N. Abdullah, S. Abdullah, M. Rusop,
Photoluminescence and Structural Properties of Gold-Assisted Zinc Oxide Nanorods, Malaysian
Journal of Science. 28 (2009) 197-201.
[14] M. Sebais, A. Chaieb, O. Halimi, L. Bouhdjer, B. Boudine, B. Sahraoui, Structural and
Optical Characterization of Hybrid Nanocomposite ZnO/PMMA, ICTON-MW. 2009, pp. 1-3.
606 Nanoscience, Nanotechnology and Nanoengineering
Nanoscience, Nanotechnology and Nanoengineering 10.4028/www.scientific.net/AMR.832 Structural and Optical Properties of ZnO/PMMA Nanocomposite 10.4028/www.scientific.net/AMR.832.602
DOI References
[4] A. Azlinda, Z. Khusaimi, S. Abdullah, M. Rusop, Characterization of Urea versus HMTA in the
Preparation of Zinc Oxide Nanostructures by Solution-Immersion Method Grown on GoldSeeded Silicon
Substrate, Advanced Material Research. 364 (2012) 45-49.
http://dx.doi.org/10.4028/www.scientific.net/AMR.364.45 [6] A. Anzlovar, K. Kogej, Z. Crnjak Orel, M. Zigon, Polyol mediated nano size zinc oxide and
nanocomposites with poly(methyl methacrylate), Express Polymer Letters. 5 (2011) 604-619.
http://dx.doi.org/10.3144/expresspolymlett.2011.59 [11] M. M. Demir, K. Koynov, U. Akbey, C. Bubeck, I. Park, I. Lieberwirth, G. Wegner, Nanocomposites as
an Effective UV Absorber with Nano Size Zinc Oxide and PMMA, Macromolecules. 40 (2007) 1089-1100.
http://dx.doi.org/10.1021/ma062184t